Uses and applications of triethanolamine oleate

1, Aqueous/oil phase emulsifier for pesticide and ink industry
2, Processing aids for pigment synthesis
3, Emulsifier for manufacturing emulsion paint

Pigment color enhancement and improve the fluidity, in the coupling solution of pigment color precipitation, add emulsifier FM3-5%, so that the fluidity of the finished pigment is significantly improved, and at the same time can improve the vividness of the pigment color. Emulsifier in the manufacture of ink, pigment grease preparation of ink, adding this product can make the grease emulsify quickly, easy to pinch and roll the pulp, can improve the luster and lubrication fluidity of ink products, the amount is generally 2-6%.

(2) ZY-1 type polymer phenolic curing agent white powder appearance
pe wax chemical formula
Softening point 90~94℃
Water content ≤0.4%
Glass transition temperature 71℃
Melting viscosity (150℃)570Pa-
Hydroxyl value 561mgKOHg
Density 1.2g/cm3
Gelation time 180℃×23s, 200℃×23s

ZY-1 type polymer phenolic curing agent is a product of Shaanxi Zhengyuan Petrochemical Co., Ltd. It is a hydroxyl-terminal resin curing agent for epoxy resin synthesized from low molecular weight epoxy resin, bisphenol A and other components. ZY-1 polymer phenolic curing agent curing anti-corrosion epoxy powder coating spoon formula and coating film performance is shown in Table 4-39 and Table 4-40.

(3) JE CP-01B, JEC
P-02B, JE CP-03B heavy anti-corrosion epoxy powder coating with curing agent
This curing agent is a compound of end-hydroxy phenolic resin and end-hydroxy polyether resin synthesized by Jiangsu and epoxy compounds, is a product developed and produced by JE CP-01A phenol Changshu Jiafa Chemical Co. for heavy anti-corrosion, with binary phenol, binary alcohol-formaldehyde epoxy resin, JE JE CP-02A2 modified phenolic epoxy resin, E-12CF epoxy resin, etc. JE CP-01B is similar to Ciba HT-3082 epoxy resin curing agent. JE CP-01B, JE CP-02B and JE CP-03B heavy anti-corrosion curing agent for heavy anti-corrosion epoxy powder
The technical index of curing agent for heavy anti-corrosion coating is shown in Table 4-41; the formulation of heavy anti-corrosion epoxy powder coating with curing agent is shown in Table 4-42; the formulation of heavy anti-corrosion epoxy powder coating with heavy anti-corrosion curing agent is shown in Table 4-42; the formulation of heavy anti-corrosion epoxy powder coating with heavy anti-corrosion curing agent is shown in Table 4-43. The gelling time and curing time of heavy anti-corrosion epoxy powder coating prepared with curing agent are shown in Table 4-43; the coating film performance of this heavy anti-corrosion epoxy powder coating is shown in Table 4-44.