Characteristics of SBS’s waterproofing roll-roofing material

The waterproofing roll-roofing material of sbs has the characteristics of weather resistance, chemical resistance and good air permeability, sbs in waterproof coating, has three major advantages of fire resistance, corrosion resistance and flame retardant. sbs modified bitumen waterproofing roll-roofing material has a waterproof layer thickness of up to 10 mm, can be used for fire protection, sbs roll-roofing material has good barrier performance, the barrier layer thickness of sbs roll-roofing material is mostly 3 mm to 6 mm.

1. The lower coating film is colorless, the upper coating film is red, the amount of modified silicone in the two coating films is the same, and the coating film is dried at 120°C for 30 minutes.

2. Measure the adhesion between layers according to GB/T9286 standard,
The following introduces anti-cratering and leveling agents such as polyether modified silicone, alternative to carnauba wax polyester modified silicone, aralkyl or alkyl modified silicone, and reactive silicone.

Polyether modified silicone
Polyether modified silicone is the most important and most used variety in modified silicone. The structural formula of polyether modified silicone is generally:
CHa「CHa[CHa] CH,
CHy-Si-O–Si-o—Si-O–Si-CH:
CHL R’J.LRJ.CH, where R’is a polyether segment-C Hz CHeO-(C Hz CHeO) -[CH.CH(CH) O], H, R are generally CH;
Some varieties are alkyl one (C Hz) mCH3.

In the structural formula of polyether silicone, the ratio of the number of dimethylsiloxane segments to the number of polyethers can affect the compatibility and at the same time affect the surface tension. The polyether segment controls the compatibility with the coating, and the dimethylsiloxane segment controls the surface tension and smoothness. The smaller the n, the larger the m, the better the leveling and smoothing effect, but the n should not be too small, otherwise it will affect the compatibility and fail to achieve the purpose of modifying polydimethylsiloxane.
By inserting different types and numbers of polyether side chains on the silicone main chain, the compatibility of silicone and coatings can be improved to varying degrees. The polyether segment is composed of ethylene oxide (EO) and/or propylene oxide (PO) units through homopolymerization or copolymerization. Polyethylene oxide is highly polar and hydrophilic, relatively speaking , Polypropylene oxide has weak polarity and is lipophilic. Adjusting the ratio of EO to PO can control or change the polarity of polyether silicone, making it suitable for systems with different polarities. Increasing the ratio of EO can increase polarity and water solubility, and thus have better compatibility with highly polar coating systems, but it also increases the tendency of foaming and foam stabilization. Conversely, increasing the ratio of PO reduces the polarity and water solubility, and at the same time reduces the tendency to foam, and has better compatibility with low-polar systems.